SINOMER® UVP4299X-3D is a polyester acrylate resin formulated for 3D printing and investment casting applications. It features high cured hardness, low yellowing tendency, and the cured coating is volatile at high temperatures.
This product is designed as an alternative to Sartomer N3D-C179.
| Parameter | Value |
|---|---|
| Appearance | Clear liquid |
| Color (APHA) | ≤ 50 |
| Viscosity (cps @ 25°C) | 90 – 180 |
| Acid Value (mg KOH/g) | ≤ 2.0 |
| Specific Gravity (g/cm³) | 1.10 ± 0.02 |
| Refractive Index (25°C) | 1.500 ± 0.005 |
| Solid Content | 100% |
Note: This data sheet is intended to give typical results, not a standard. Subject to COA.
High cured hardness
Low yellowing tendency
Suitable for high-temperature volatilization after curing
Designed as an alternative to Sartomer N3D-C179
3D printing casting patterns
Investment casting
Light source: LED is the primary curing source for current UV printers
Compatible with: LCD printer systems
Recommended exposure: 4 seconds at 100W for optimal results
| Step | Process |
|---|---|
| 1 | Design & 3D printing |
| 2 | Investment casting |
| 3 | Clean burnout – temperature ramp to 600–800°C, process duration 2–3 hours |
| 4 | Cooling & dissolving |
| 5 | Finished product |
Ultrasonic cleaning pool (to remove residual resin)
Post-curing oven (for additional light curing to achieve desired properties)
Base formulation:
| Component | Percentage |
|---|---|
| SINOMER® UVP4299X-3D | 97% |
| SINOCURE TPO (or SINOCURE 2425) | 3% |
For faster curing:
| Modification | Note |
|---|---|
| Replace 30–40% of UVP4299X-3D with SINOMER EO3-TMPTA | Increases cure speed |
| Replace up to 10% of UVP4299X-3D with SINOMER DPHA | For even faster curing |
25 kg or 200 kg / drum
Store in a dry, clean, well-ventilated warehouse.
Avoid exposure to light and heat.
Protect from leakage, rain, and direct sunlight during transportation.
A: Yes. It is designed as an alternative to Sartomer N3D-C179.
A: It is compatible with LCD printer systems. LED is the primary light source for current UV printers.
A: 4 seconds at 100W.
A: The temperature should be ramped to 600–800°C, with a process duration of 2–3 hours.
A: An ultrasonic cleaning pool for removing residual resin and a post-curing oven for additional light curing.
A: 97% UVP4299X-3D + 3% SINOCURE TPO (or SINOCURE 2425).
A: Replace 30–40% of UVP4299X-3D with SINOMER EO3-TMPTA. For even faster curing, replace up to 10% with SINOMER DPHA.
A: 12 months from the date of manufacture when stored in original unopened packaging under recommended conditions.
A: Yes. Solid content is 100%.
A: Store in a dry, clean, well-ventilated warehouse, away from light and heat. Keep containers tightly sealed when not in use.
Sinocure Chemical Group
No. 61, South Industrial Road, Jinan Area of Shandong Pilot Free Trade Zone, China
Email: Info@sinocurechem.com | Tel: +86 15668330235
Website: www.sinocurechem.com
This document is for informational purposes only. Users should conduct their own testing to determine suitability for their specific applications. SINOMER® is a registered trademark of Sinocure Chemical Group. Sartomer® is a trademark of Arkema Group.