AgeSin® Coating and Ink Additives

AgeSin® LA-D887BR

AgeSin® LA-D887BR is a Leveling Agent with Fluorocarbon modified polyacrylate copolymer solution .Can completely replace Basf EFKA3777.(Better defoaming than Basf EFKA3777)

Send Enquiry

AGESIN® Fluorocarbon modified polyacrylate copolymer solution

Product Number: AgeSin® LA-D887BR

Equivalent alternativesBasf EFKA3777 (Better defoaming than Basf EFKA3777))


Composition Fluorocarbon modified polyacrylate copolymer solution

Transparent to slight yellowish clear liquid

Solvent Di-basic ester/ S-150
Active substance 70%
Density 0.96-1.00g/ml(25±1)℃
Viscosity 50-1000mPa·s
(Rotational viscometer)(25±0.2)℃
Flash point 62>℃

Note: This data sheet is intended to give typical results, not standard.Subject to COA.

Application system
Excellent anti-foaming and foam-inhibition.
Fast leveling speed.
Good long-wave leveling. Prevent orange peel phenomenon.
Be suitable for roil&roll coating, epoxy floor coating. Not suit for varnish and UV cure system.
In order to improve the ability of anti-foaming, should be added to the mill.
Suggest addition
Addition to total formulation    0.2-0.8%
Storage stability
Keep intact 24 months in original package.Products beyond the storage period may continue to be used after inspection. The container must be closed immediately after use.

Applicate recommendation

Transparency in varnish 0
Defoaming 4
Dynamic surface tension 2
Static surface tension 2
Slip 5

0=unavailable 5=very effective


25KG / 180KG


Being kept in dry, clean warehouse with well ventilation.

Avoid exposing to light and heating.

Protecting the product from leakage, rain and insolation during transportation.


Product description:

Fluorocarbon modified polyacrylate copolymer solution

Equivalent alternatives

Basf EFKA3777

Application system



Di-basic ester/ S-150


50-1000mPa·s(Rotational viscometer)(25±0.2)℃


25KG or 180KG/drum